Polymaker Fiberon™ PA6-CF20 1.75mm | 500g

Sale!

~~£44.99~~ £39.99

colour

Quantity

Item number: 6938936714613

Key Features:

Reinforced with 20% carbon fibres
Significantly improved stiffness and strength
High heat resistance [heat deflection temperature of up to 215 °C]
Outstanding layer adhesion with Fiber Adhesion™ Technology

Application:

Automotive
Industrial parts
Composite Manufacturing

Description

Polymaker Fiberon™ PA6-CF20 is a 20% carbon fiber reinforced Nylon 6 filament. The carbon fiber reinforcement provides significantly improved stiffness, strength and heat resistance with outstanding layer adhesion thanks to Fiber Adhesion™ Technology. PA6-CF outperforms almost every 3D printing material, offering extreme durability and functionality while featuring a heat deflection temperature of 215°C.

Specification

Diameter	1.75mm
Diameter Tolerance	± 0.02mm
Net weight	500grams

Recommendation

Temperature

Printing Temp:- 280 - 300˚C

Bed Temp:- 40 - 50°C

Printing Speed

Up to 300mm/s

Fan Speed

Closed Chamber

Not required

Surface

Adhesive

Drying

100˚C / 10h (Only if the material has absorbed moisture)

Nozzle

All-metal hotend above 280˚C and Hardened nozzle

Note

Abrasion of the brass nozzle happens frequently when printing Fiberon™ PA6-CF20. Normally, the life of a brass nozzle would be approximately 9h. A wear-resistance nozzle, such as hardened steel and ruby nozzle, is highlyrecommended to be used with Fiberon™ PA6-CF20.

Fiberon™ PA6-CF20 is sensitive to moisture and should always be stored and used under dry conditions (relative humidity below 20%).

If Fiberon™ PA6-CF20 is used as the support material for itself, please remove the support structure before excessive moisture absorption. Otherwise, the support structure can be permanently bonded to the model.

After the printing process, it is recommended to anneal the model in the oven at 100°C for 16 hours.